| Bond strength table 1bs/in2（kg/cm2） |
| |
2 hours |
24 hours |
72 hours |
| PS |
500（35.2） |
1200（84.5） |
1800（126.8） |
| Sample thickness:0.25 in (0.64cm) Bonding area:1.0 in2(6.45cm2) |
|
|
| Working Time（working temperature：25℃/75℉） |
| Working Time |
Set Time |
Time to reach 80% strength |
| 10 min |
4 hours |
24 hours |
|
| 24 hours at 75℉ (25℃) |
| Bonding Material |
Lap-shear Strength Mpa/Psi |
Failure Mode |
| PP |
8 (1160) |
Cohesive |
| PE |
7 (1000) |
Substrate |
| PTFE |
5 (725) |
Adhesive |
| PMMA |
7 (1000) |
Adhesive |
| Aluminum |
6 (870) |
Adhesive |
| Stainless Steel |
7 (1000) |
Adhesive |
| Service Temperature: 32℉ to 104℉ (0℃ to 40℃) |
GP505 can be fast cured by chemical reaction and it can achieve to a very high strength after 24 to 48 hours, the bonding strength will continue to be increased in the later few weeks.
It is specially designed for high-strength structural bonding among PE, PP, PVDF, PTFE and metals.